REFRACTORIES FOR ALUMINIUM FOUNDRIES
######################################################################
Refractories for Crucible Furnaces
######################################################################
FURCAST LC-85
Alumina based, low cement refractory castable for the permanent refractory lining in crucible furnaces for copper and its alloys.
High refractoriness and very good behaviour througout thermal cycles.
- Density: 2,60 Kg/dm3
- Thermal conductivity: 2,20 W/m.K
THERMOCAST-85
Insulating, refractory castable cement based on Alumina for the permanent refractory lining of crucible furnaces for copper and its alloys.
High refractoriness and very good insulating behaviour for minimum side thermal losses in the furnace.
- Density: 2,0 Kg/dm3
- Thermal conductivity: 1,50 W/m.K
######################################################################
Refractories for casting ladles
######################################################################
ALUCAST 80
Alumina based, low cement refractory castable for the permanent refractory lining in crucible furnaces for aluminium and its alloys.
High refractoriness and very good behaviour throughout thermal cycles.
- Density : 2,60 Kg/dm3
- Thermal conductivity : 2,20 W/m.K
######################################################################
SILICAST 80S
Insulating, refractory castable material based on Fused Silica, with exceptional thermal stability.
- Density : 2,0 Κg/dm3
- Thermal conductivity: 1,50 W/m.K
Provides a smooth and clean surface, maintained for multiple castings, ensuring a clean and slag-free metal for casting.
######################################################################
SILICAST 101/SF
Self flowing, insulating refractory castable material based on Fused Silica, with exceptional thermal stability.
Flows without vibration.
- Density : 2,0 Κg/dm3
- Thermal conductivity: 1,20 W/m.K
Provides a smooth and clean surface, maintained for multiple castings, ensuring a clean and slag-free metal for casting.
######################################################################